ZIRCONIA DISCS DIGITECH are designed to provide the best results in your restorations.
Made with the best ZIRCONIA powder providing excellent performance and milling precision.
Offered in all platforms 98.5mm 98mm 95mm 71mm and Cerec compatible.
ALL our DIGITECH ZIRCONIA MILLING DISCS
are manufactured with :
* First grade ZIRCONIA powder
* Shrinkage adjusted for 20%
DIGITECH ZIRCONIA DISCS counts with the following types of material :
4D ST MULTILAYER
ST SUPER TRANSLUCENT
TT Anterior Translucency
HS High Strength
Characteristics DIGITECH ZIRCONIA MILLING DISCS
DIGITECH 4D Functional MULTILAYER
New Generation MULTILAYER DISCS .
Overall strength 1027 – 1300 mpa
DIGITECH 4D disc, is a 5 layers dental MULTILAYER zirconium oxide with gradient translucency, color and high translucency.
layer 1 1027 mpa 46.6% translucency
layer 2 1105 mpa 45.6% translucency
layer 3 1205 mpa 44.3% translucency
layer 4 1300 mpa 43.0% translucency
layer 5 1300 mpa 43.0% translucency
Advantages of 4D MULTILAYER ZIRCONIA DISCS:
Natural color gradient
Translucency gradient with special adjustment
16 Vita shades + 4 bleach shades
DIGITECH HS Mono white
The DIGITECH High Strength ZIRCONIA blanks used for monolithic or anatomically reduced anterior restorations and framework bridge combined with porcelain.
With high strength (more than 1400Mpa) and good TRANSLUCENT(39%) it offers to the labs with its high strength and good TRANSLUCENT.
DIGITECH ST SUPER TRANSLUCENT ( mono and MULTILAYER )
DIGITECH SUPER TRANSLUCENT MULTILAYER disc is SUPER high TRANSLUCENT ZIRCONIA with integrated shade and translucency of 5 layers gradient. Natural color and TRANSLUCENT gradient simulate tooth enamel, dentine and cervical shades. Simply operation for dental technician without staining.
• SUPER strength more than 1100Mpa and SUPER TRANSLUCENT more than 43%
• Available for 16 shades
• Natural simulate teeth after sintering
• Fully anatomical crowns and multi-unite bridges
DIGITECH TT Anterior Translucency
DIGITECH Anterior Top TRANSLUCENT with ultra TRANSLUCENT previously only known in lithium disilicate. With 49% transmits and more than 600 PMA, It is best choice for anterior , posterior restoration, veneer, onlay, inlay and high esthetic restoration up to 3 unite bridge.
Ultra TRANSLUCENT ZIRCONIA for highly esthetic anterior and posterior regions
Firing Chart DIGITECH ZIRCONIA MILLING DISCS
* Starting temperature: Room Temperature
* Temperature Heating rate 4 Celcius per minute
* Sinterization temperature
HS and ST 1530 Celsius 2 hours
AT 1450 Celcius 2 hours
* Temperature Coling Rate 4 Celcius per minute
* Total Cycle time: 16 hours .
Then open door, don't forget to decontaminate your sinter oven once a week, or at least once a month. This advice is for every sinter oven in the market, regardless of brand name, or origin.